A two pack epoxy primer with low VOC, good corrosion resistance, good long-term weathering protection and fast drying
For use as a primer for the temporary protection of blasted steel prior to the application of a wide range of products.
Part B (Curing Agent) 5748
Volume Solids 61% ±2% (ASTM D2697-86)
Mix Ratio 1 volume(s) Part A to 1 volume(s) Part B
Typical Film Thickness 75 microns dry (123 microns wet), 50 - 75 microns dry practical range equivalent to 82 - 123 microns wet
Theoretical Coverage 8.13 m²/litre at 75 microns dft, allow appropriate loss factors
Method of Application Airless Spray, Brush, Conventional Spray, Roller
Flash Point (Typical) Part A 37°C; Part B 39°C; Mixed 37°C (Setaflash) (ASTM D-3278)
Induction Period 2 hours @ 10 - 16°C; 1.5 hours @ 16 - 21°C; 0.5 hours above 21°C.