A quick drying two pack epoxy holding primer / tie coat which is suitable for overcoating after extended periods of weathering.
For use as a primer for the protection of prepared steel prior to the application of a wide range of products. Can also be used as a tie coat for application to freshly applied zinc primers to prevent zinc salt formation on weathering and to reduce pinholing of subsequent applied coatings. Suitable for use with controlled cathodic protection.
For use at Newbuilding, Maintenance & Repair or On Board Maintenance.
Finish/Sheen Not applicable
Part B (Curing Agent) EGA089
Volume Solids 47% ±2% (ISO 3233:1998)
Mix Ratio 4.00 volume(s) Part A to 1 volume(s) Part B
Typical Film Thickness 1.6 mils dry (3.4 mils wet)
Theoretical Coverage 471 ft²/US gal at 1.6 mils dft, allow appropriate loss factors
Method of Application Airless Spray, Brush, Conventional Spray, Roller
Flash Point Part A 79°F; Part B 77°F; Mixed 79°F
Induction Period Not required